Copper-Nickel Alloy Cu90/Ni10

Key Features:

  1. Copper-Nickel Alloy 90/10 has good high temperature strength
  2. Excellent resistance to fresh, brackish & marine water corrosion
  3. Prevents metal loss due to phosphoric, sulfuric and organic acids
  4. Avoids attack by alkali chlorides, sulfates, ammonia & its extracts
PDF Download

About Copper-Nickel Alloy Cu90/Ni10

Copper-Nickel Alloy 90/10 (Cu 90%, Ni 10%) is an economical alternative to Cu-Ni 70/30 alloy. It has additional composition of iron 1.4 % to provide increased resistance to general corrosion, erosion and impingement corrosion. It should not be used in chromic, hydrochloric and nitric acids and extensively polluted water with sewage and industrial garbage.

90/10 Cu Ni alloy can be formed by hot and cold processing techniques. Fine weldability. It can be used to prevent corrosion by turbulent and high velocity seawater. It has low temperature coefficient of electric resistance. Good ductility. Cu Ni alloy 90/10 doesn’t need surface protection therefore it assures additional security. It is an ideal metal for piping in the ship manufacturing industry as it has good resistance to stress corrosion cracking in ammonized marine water. Further it resists pitting & crevice corrosion.

Copper-Nickel Alloy 90/10 Industrial Nomenclatures: CN102, C70600, C70610, CW352H, DEF STAN 02-879, BS2870, BS2874, ASTM B151, EN 12163, 2.0872, NF A51-115, CuNi10Fe1Mn

Cupronickel Alloy 90/10 Specifications

ASME SB111, SB171, SB359, SB395, SB466, SB467, SB543, ASTM B111, B122, B151, B171, B359, B395, B432, B466, B467, B543, B608, DIN 2.0872, MIL C-15726, T-15005, T-16420, T-22214, SAE J461, J463

Copper-Nickel Alloy 90/10 Applications

Seawater hardware, offshore site seawater pipes, propellers, boats, crankshafts, tidewater based power production units, desalination systems, oil refining and chemical processing, condenser tubes, plates, distiller tubes, condenser baffles, heat exchanger components, evaporators, saltwater pipes, water containers, brakes and hydraulic suspension equipments, automotive quenching systems, production of coins and medals

90- 10 Cu Ni Alloy heat processing

Generally the heat processing is only followed for soft annealing and stress relaxation in Copper-Nickel alloys. Recrystalizaiton annealing temperatures vary from 620oC to 900oC on the base of extent of cold processing, magnitude of nickel and other elements. Elevated temperatures are lined with small annealing periods and low temperatures with prolong annealing periods. The stress relaxation annealing is conducted from 280oC to 500oC. It is recommended to anneal alloy 90/10 in unaerated or in a nominal reducing condition.

Forms Produced

90- 10 Cu Ni Alloy Wire 90- 10 Cu Ni Alloy Wire Mesh
90- 10 Cu Ni Alloy Strip 90- 10 Cu Ni Alloy Sheet/Plate
90- 10 Cu Ni Alloy Rod/Bar 90- 10 Cu Ni Alloy Pipe
90- 10 Cu Ni Alloy Flanges  90-10 Cu-Ni Alloy Foil

 